前言：ABS，台湾奇美，PA-747S，本白，高刚性，高流动，电子电器部件，板材级
物理性能额定值单位测试方法
| 熔体流动速率 (220℃×10kg) | 7.5 | g/10min | ASTM D-1238 |
| 比重 | 1.03 | 23/23℃ | ASTM D-792 |
| 熔体流动速率 (200℃×5kg) | 0.7 | g/10min | ASTM D-1238 |
机械性能额定值单位测试方法
| 弯曲强度 | 620 | Kg/cm | ASTM D-790 |
| IZOD冲击强度 (1/4") | 6.5 | ft.lb/in | ASTM D-256 |
| 洛氏硬度 | 102 | R | ASTM D-785 |
| 引张强度 | 5530 | lb/in | ASTM D-638 |
| IZOD冲击强度 (1/8") | 40 | kg.cm/cm | ASTM D-256 |
| 弯曲强度 | 8800 | lb/in | ASTM D-790 |
| 弯曲弹性率 | 3.0×105 | lb/in | ASTM D-790 |
| 引张强度 | 390 | Kg/cm | ASTM D-638 |
| 弯曲弹性率 | 2.1×104 | Kg/cm | ASTM D-790 |
| 伸长率 | 40 | % | ASTM D-638 |
| IZOD冲击强度 |
|
| ASTM D-256 |
| (1/4") | 35 | kg.cm/cm |
|
| (1/8") | 7.5 | ft.lb/in |
|
热性能额定值单位测试方法
| 维卡软化点 | 103 | ℃ | ASTM D-1525 |
| 热变形温度 | 87(189) | ℉ | ASTM D-648 |
| 燃烧性 (File No. E56070 UL&C-UL) | - | 1/16"HB |
|
| 维卡软化点 | 217 | ℉ | ASTM D-1525 |
| 热变形温度 | 97(206) | ℃ | ASTM D-648 |