前言：POM，7520，日本旭化成，高流动，包装容器，塑料容器，薄壁制品，注塑
| 吸湿率 | 0.2 | % | ASTM D-570 |
| 熔体流动速率 | 30 | gr/10min | ASTM D-1238 |
| 成型收缩率 | 1.6-2.0 | % | 旭化成方法 |
| 磨耗率 | 14 | mg/1000次 | ASTM D-1044 |
| 比重 | 1.41 | ASTM D-792 |
| 延伸率 | 50 | % | ASTM D-638 |
| 洛氏硬度 | 80 | M scale | ASTM D-785 |
| 抗挠系数 | 2630 | MPa | ASTM D-790 |
| 洛氏硬度 | 115 | R scale | ASTM D-785 |
| 抗挠强度 | 90 | MPa | ASTM D-790 |
| 拉伸强度 | 61 | MPa | ASTM D-638 |
| 悬臂梁式缺口冲击强度 | 59 | J/M | ASTM D-256 |
| 热变形温度 | ASTM D-645 | ||
| (0.45MPa) | 158 | ℃ | |
| (1.82MPa) | 110 | ℃ | |
| 阻燃性 | HB | UL 94 | |
| 线性膨胀系数 | 10 | ×10-5cm/cm℃ | TMA |