基本性能额定值单位测试方法比重1.42g/cm³ASTM D792, ISO 1183熔体质量流动速率2.8g/10 minASTM D1238 (190℃/2.16kg)2.8g/10 minISO 1133成型收缩率 (flow)1.8 to 2.2%ASTM D955, ISO 294-4 (Across flow)1.8 to 2.2%ISO 294-4吸水率 (24hr)0.20%ASTM D570洛氏硬度ASTM D785 (M-Scale)94 (R-Scale)120机械性能额定值单位测试方法拉伸模量3100MPaISO 527-2拉伸应力 (Yield)71.0MPaISO 527-268.0MPaASTM D638拉伸伸长率 (Break)75%ASTM D638 (Break)65%ISO 527-2弯曲模量2740MPaASTM D790弯曲强度98.0MPaASTM D790泰伯磨耗量 (1000次)13.0mgASTM D1044夏比缺口冲击强度 (23°C)13kJ/m²ISO 179/1eAIZOD缺口冲击强度108J/mASTM D256热性能额定值单位测试方法热畸变温度ASTM D648 (0.45MPa,未退火)172°C (1.8MPa,未退火)133°C (0.45MPa,未退火)163°C (1.8MPa,未退火)96.0°C线性热膨胀系数 (flow)0.00010cm/cm/°CASTM E831其它性能额定值单位测试方法阻燃等级HBUL 94