| 比重 | 0.902 | g/cm | ASTM D792 |
| 熔流率 (190℃/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| 门尼粘度 (ML 1+4, 121℃) | 10 | MU | ASTM D1646 |
| 硬度计硬度 | |||
| (邵氏 A, 1 秒, 模压成型) | 90 | ASTM D2240 | |
| (邵氏 D, 1 秒, 模压成型) | 41 | ASTM D2240 | |
| 拉伸模量 (**** 正割 (模压成型)) | 7.30 | MPa | ASTM D638 |
| 抗张强度 (断裂, 模压成型) | 22.4 | MPa | ASTM D638 |
| 伸长率 (断裂, 模压成型) | 750 | % | ASTM D638 |
| 弯曲模量 | |||
| (1% 正割: 模压成型) | 76.3 | MPa | ASTM D790 |
| (2% 正割: 模压成型) | 75.6 | MPa | ASTM D790 |
| 撕裂强度 | 90.2 | kN/m | ASTM D624 |
| 玻璃转化温度 | -32.0 | ℃ | Internal Method |
| 维卡软化温度 | 84.0 | ℃ | ASTM D1525 |
| 溶融温度 | 97.0 | ℃ | Internal Method |
| 结晶峰温 | 80.0 | ℃ | Internal Method |