前言：LG化学，HI100Y，注塑级，ABS，透明级，增强级，高抗冲，阻燃级，塑胶原料
基本性能额定值单位测试方法
| 熔体流动速率 (220℃/10kg) | 20 | g/10min | ASTM D-1238 |
物理性能额定值单位测试方法
| 比重 | 1.02 |
| ASTM D-792 |
| 模具收缩率 | 0.4-0.7 | % | ASTM D-955 |
机械性能额定值单位测试方法
| 拉伸屈服强度 (50mm/min) | 380 | Kg/cm | ASTM D-638 |
| 拉伸模量 (1mm/min) | 16000 | Kg/cm | ASTM D-638 |
| 断裂伸长率 (50mm/min) | 40 | % | ASTM D-638 |
| 弯曲强度 (15mm/min) | 600 | Kg/cm | ASTM D-790 |
| 弯曲模量 (15mm/min) | 19000 | Kg/cm | ASTM D-790 |
| IZOD缺口冲击强度 |
|
| ASTM D-256 |
| (1/4",23℃) | 40 | kg.cm/cm |
|
| (1/4",-30℃) | 28 | kg.cm/cm |
|
| (1/8".23℃) | 45 | kg.cm/cm |
|
| (1/8".-30℃) | 33 | kg.cm/cm |
|
| 洛氏硬度 | 90 | R-Scale | ASTM D-785 |
热性能额定值单位测试方法
| 热变形温度 |
|
| ASTM D-648 |
| (未退火.18.5kg/cm,1/4") | 84 | ℃ |
|
| (未退火.4.6kg/cm,1/4") | 88 | ℃ |
|
| 维卡软化点 (5kg.50℃) | 93 | ℃ |
|