前言：PP，聚丙烯，BJ500，韩华道达尔，高抗冲，电子电器部件，注塑
| 熔体流动速率 (230℃.2.16kg) | 10 | g/10min | ASTM D-1238 |
| 密度 | 0.91 | g/cm | ASTM D-1505 |
| 抗张强度 | ASTM D-638 | ||
| (50mm/min) | 300 | KG/cm | |
| (50mm/min) | 200 | KG/cm | |
| IZOD冲击强度 (1/4".0℃) | 6 | kg.cm/cm | ASTM D-256 |
| 洛氏硬度 (23℃) | 85 | R Scale | ASTM D-785 |
| IZOD冲击强度 (1/4".23℃) | 10 | kg.cm/cm | ASTM D-256 |
| 断裂伸长率 (50mm/min) | ＞300 | % | ASTM D-638 |
| 弯曲模量 | 13500 | kg/cm | ASTM D-790 |
| IZOD冲击强度 (1/4".-20℃) | 5 | kg.cm/cm | ASTM D-256 |
| 可燃性 (1/8") | HB | UL 94 | |
| 维卡软化点 (1kg) | 152 | ℃ | ASTM D-1525 |
| 可燃性 (1/16") | HB | UL 94 | |
| 热变形温度 (4.6kg/cm(1/8")) | 110 | ℃ | ASTM D-648 |
| 熔点 (DSC) | 160 | ℃ | SGC |