前言：海翠料，TPEE，LG化学 BT，1140D，高温TPEE，挤出押出芯线
| 熔体流动速率 (200℃/2.16kg) | 10 | g/10min | ASTM D1238 |
| 比重 | 1.16 | g/cm | ASTM D792 |
| 吸水率 (24hr.23℃) | 0.6 | % | ASTM D570 |
| 成型收缩率 | 0.8 | % | ASTM D955 |
| 拉伸强度 (Yield) | 5.90 | MPa | ASTM D638 |
| 弯曲模量 | 59 | MPa | ASTM D790 |
| 拉伸伸长率 (Break) | 900 | % | ASTM D412 |
| 断裂强度 | 128 | KN/m | ASTM D624 |
| 热变形温度 (0.45MPa.Uaannealed) | 65 | ℃ | ASTM D648 |