前言：PA66，日本旭化成，FG170，增强级PA66，加纤15%，阻燃防火V0级，耐高温
| 吸湿率 (湿) | 0.9 | % |
| 成型收缩率 | 0.6-1.0 | % | 旭化成方法 |
| 磨耗率 (湿) | 24 | ×10-6kg/1000times | ASTM D-1044 |
| 比重 (干) | 1.48 | ASTM D-792 |
| 洛氏硬度 (干(湿)) | 95(55) | M scale | ASTM D-785 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 49(59) | J/M | ASTM D-256 |
| 抗挠强度 (干(湿)) | 191(152) | MPa | ASTM D-790 |
| 断裂延伸率 (干(湿)) | 2.5(2.7) | % | ASTM D-638 |
| 拉伸强度 (干(湿)) | 132(108) | MPa | ASTM D-638 |
| 抗挠系数 (干(湿)) | 6.4(4.9) | GPa | ASTM D-790 |
| 热变形温度 (1.82MPa,干) | 248 | ℃ | ASTM D-648 |
| 阻燃性 (干) | V-0 | UL 94 | |
| 热变形温度 (0.46MPa,干) | 255 | ℃ | ASTM D-648 |
| 线性膨胀系数 (干) | 3 | ×10-5/K | ASTM D-696 |
| 氧指数 (干) | 38 | % | ASTM D-2863 |