前言：PP，乐天化学，JI-320，高抗冲，高刚性，热稳定，高强度，汽车家电部件
| 熔体流动速率 | 1.5 | g/10min | ASTM D-1238 |
| 密度 | 0.90 | g/cm | ASTM D-1505 |
| 成型收缩率 | 1.6-1.8 | % | HPC Method |
| 冲击强度 | ASTM D-256 | ||
| 4.5 | kg·cm/cm | ||
| 13.0 | kg·cm/cm | ||
| 拉伸屈服强度 | 290 | Kg/cm | ASTM D-638 |
| 最终拉伸率 | >500 | % | ASTM D-638 |
| 洛氏硬度 | 95 | R | ASTM D-785 |
| 弹性挠曲模量 | 14,000 | Kg/cm | ASTM D-790 |
| 热变形温度 | 125 | ℃ | ASTM D-648 |
| 维卡软化点 | 145 | ℃ | ASTM D-1525 |
| 耐热性 (130℃老化) | >3,000 | hour | HPC Method |