前言：韩国sk，H900F，韩国注塑级，热稳定性，高刚性，抗静电
| 熔体流动速率 | 0.5 | g/10min | ASTM D-1238 |
| 弯曲弹性系数 | 15000 | kg/cm | ASTM D-790 |
| IZOD缺口冲击强度 (23℃) | 7 | kg.cm/cm | ASTM D-256 |
| 洛氏硬度 | 97 | R Scale | ASTM D-785 |
| 断裂伸长率 | >500 | % | ASTM D-638 |
| 拉抻断裂强度 | 360 | kg/cm | ASTM D-638 |
| 维卡软化点 | 152 | ℃ | ASTM D-1525 |
| 流动性 | 400 | mm | SK |
| 加速老化时间 | 360 | % | SK |
| 热变形温度 | 105 | ℃ | ASTM D-648 |