前言：日本旭化成，14G25，玻纤增强25%，耐高温，高刚性，增强级尼龙，注塑级
| 吸湿率 (湿) | 1.9 | % |
| 成型收缩率 (干) | 0.5/0.9 | % | 旭化成方法 |
| 比重 (干) | 1.32 | ASTM D-792 | |
| 磨耗率 (湿) | 12 | ×10-6kg/1000times | ASTM D-1044 |
| 断裂延伸率 (干(湿)) | 3(6) | % | ASTM D-638 |
| 洛氏硬度 | ASTM D-785 | ||
| (干(湿)) | 120(-) | R scale | |
| (干(湿)) | 96(74) | M scale | |
| 拉伸强度 (干(湿)) | 180(110) | MPa | ASTM D-638 |
| 抗挠强度 (干(湿)) | 290(175) | MPa | ASTM D-790 |
| 抗挠系数 (干(湿)) | 8.1(4.7) | GPa | ASTM D-790 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 105(160) | J/M | ASTM D-256 |
| 阻燃性 (干) | HB | UL 94 | |
| 热变形温度 (1.82MPa,干) | 250 | ℃ | ASTM D-648 |
| 线性膨胀系数 (干) | 3 | ×10-5/K | ASTM D-696 |
| 导热率 (干) | 0.3 | W/(m.k) | |
| 热变形温度 (0.46MPa,干) | 260 | ℃ | ASTM D-648 |