前言：POM，5050，日本旭化成POM，高流动，低粘度，高结晶率，高硬度
| 吸湿率 | 0.2 | % | ASTM D-570 |
| 熔体流动速率 | 21 | g/10min | ASTM D-1238 |
| 比重 | 1.42 | ASTM D-792 | |
| 磨耗率 | 13 | mg/1000cycles | ASTM D-1044 |
| 成型收缩率 | 1.7-2.1 | % | 旭化成方法 |
| 洛氏硬度 | 120 | R Scale | ASTM D-785 |
| 延伸率 | 45 | % | ASTM D-638 |
| 抗挠系数 | 2940 | MPa | ASTM D-790 |
| 拉伸强度 | 69 | MPa | ASTM D-638 |
| 悬臂梁式缺口冲击强度 | 59 | J/m | ASTM D-256 |
| 抗挠强度 | 103 | MPa | ASTM D-790 |
| 洛氏硬度 | 94 | M Scale | ASTM D-785 |
| 热变形温度 | ASTM D-648 | ||
| (0.45MPa) | 172 | ℃ | |
| (1.82MPa) | 136 | ℃ | |
| 燃烧性 | HB | UL 94 | |
| 线性膨胀系数 | 10 | ×10-5cm/cm℃ | TMA |