前言：PP，韩华道达尔，RJ500，耐高温，高流动，高刚性，聚丙烯
| 熔体流动速率 (230℃,2.16kg) | 10 | g/10min | ASTM D-1238 |
| 密度 | 0.91 | g/cm | ASTM D-1505 |
| 模具收缩率 (2mm(t)) | 1.5-1.8 | % |
| 弯曲模量 | 11000 | kg/cm | ASTM D-790 |
| 断裂伸长率 | >600 | % | |
| IZOD冲击强度 (1/4",-20℃) | 2 | kg·cm/cm | ASTM D-256 |
| 抗张强度(断裂) | 350 | ||
| 洛氏硬度 (23℃) | 85 | R scale | ASTM D-785 |
| 抗张强度(屈服) (50mm/min) | 330 | kg/cm | ASTM D-638 |
| 热变形温度 (4.6kg/cm(1/8")) | 95 | ℃ | ASTM D-648 |
| 维卡软化点 (1kg) | 125 | ℃ | ASTM D-1525 |
| 熔点 (DSC) | 150 | ℃ | SGC |